Conductive, good corrosion resistance, good
thermal conductivity, functional ceramics, low
mechanical characteristics, relatively high
hardness. |
|
|
|
|
|
|
Technical Parameters |
|
|
|
|
|
| |
|
Description |
Unit |
Value |
|
Material |
|
TiO2 95% |
|
Colour |
|
black |
|
Density |
g/cm3 |
4.0 |
|
Flexural Strength |
MPa |
70 |
|
Compressive Strength |
MPa |
600 |
|
Modulus of Elasticity (young) |
GPa |
- |
|
Impact Resistance |
MPa m1/2 |
- |
|
Weibull Modulus |
m |
- |
|
Vickers Hardness |
HV 0.5 |
900 |
|
Thermal Expansion Coefficient |
10-6 K-1 |
8.5 |
|
Thermal Conductivity |
W/mK |
25 |
|
Thermal Shock Resistance |
∆T °C |
- |
|
Maximum Use Temperature |
°C |
- |
|
Volume Resistivity at 20 °C |
Ωcm |
>102 |
|
Dielectric Strength |
kV/mm |
- |
|
Open Porosity |
% |
0 |
|
Dielectric Constant |
εr |
- |
|
Dielectric Loss Angle |
tanδ |
- |
|
|
|
|
|
|
|
|
|
These properties were
measured on test samples. The values are typical
material properties and may vary according to
product configuration, geometry and
manufacturing process." |
|
|
|
|
|
| |
|
|
|
|
|
| |
 |
|
|
|
|
|
| |
Electrically insulating,
good corrosion resistance, good thermal
conductivity, functional ceramics, low mechanical
characteristics, relatively high hardness.
|
|
|
|
|
|
|
Technical Parameters |
|
|
|
|
| |
|
Description |
Unit |
Value |
|
Material |
|
TiO2 95% |
|
Colour |
|
yellow |
|
Density |
g/cm3 |
4.0 |
|
Flexural Strength |
MPa |
70 |
|
Compressive Strength |
MPa |
600 |
|
Modulus of Elasticity (young) |
GPa |
- |
|
Impact Resistance |
MPa m1/2 |
- |
|
Weibull Modulus |
m |
- |
|
Vickers Hardness |
HV 0.5 |
900 |
|
Thermal Expansion Coefficient |
10-6 K-1 |
8.5 |
|
Thermal Conductivity |
W/mK |
25 |
|
Thermal Shock Resistance |
∆T °C |
- |
|
Maximum Use Temperature |
°C |
- |
|
Volume Resistivity at 20 °C |
Ωcm |
>1010 |
|
Dielectric Strength |
kV/mm |
- |
|
Open Porosity |
% |
0 |
|
Dielectric Constant |
εr |
- |
|
Dielectric Loss Angle |
tanδ |
- |
|
|
|
|
|
|
|
|
|
These properties were
measured on test samples. The values are typical
material properties and may vary according to
product configuration, geometry and
manufacturing process. |
|
|
|
|
|
|